Product Specifications

Viscosity:	Flash Point:	Density (Kg/L):	Solid (% by weight):	Solid (% by volume):	Shelf Life (months):
Zahn #2 signature cup 35 sec at 25°C	-20°C	1.04 ± 2% at 25°C	40%	27%	12

Product Description

Danspeed White is a pigmented post-catalyzed Reactive Amino Coating (RAC) with very good light stability based on the choice of resin used in the product. Danspeed White gives a smooth, knock proof and hard-wearing surface resisting influence from alcohol, water, etc

Special recognition: when applied as specified, will meet required performance for the ANSI/KCMA A161.1 1990 9.0 Finish Test.

Uses

This product is used as the final coat over wood, plywood, chipboard, etc., meant for interior use. This product is recommended for kitchen cabinets, high build office or residential furniture as well as many other interior wood applications where high durability is required.

Environmental Data (as supplied)

VOC less exempt lb/gal:	VOC lb/gal:	VOC less exempt g/l:	VOC g/l:	VOC lb/lb Solid:	VHAPs lb/lb Solid:
5.09	4.83	611	580	1.39	0.62

Note:

See individual compliance sheets for specific data

Application Data

Suggested Uses:	Mixing Ratio:	Pot Life:	Application Viscosity:	Reducer:	Retarder:	Clean-up Solvent:	Recommended Wet Film:	Coverage:
Spray	10% 999-031A	4 hours	22-30 sec Zahn #2 at 25°C	121-803 or 121-8020 as needed	800-5328 EEP	Lacquer Thinner	3 to 5 mils wet	11 m2/l (115 pi2/l) at 1 mil dry and at 100% efficiency. Coverage will vary depending on method of application or coating thickness.

Note:

N/A

Surface Preparation

Primer must be sanded with a #280/320 grit stearated paper before application of the topcoat and must be free of dirt and any other contamination. Primer must be recovered within 8 hours after sanding. Danspeed White must not be applied over metal, old finish or nitrocellulose lacquer.

General Information

Catalyze and reduce the material as recommended. To ensure proper sheen, the catalyzed material should be agitated at all times. Danspeed White must be thoroughly stirred while adding catalyst and thinner in the recommended mixing ratio. Apply 3-5 mils wet on sanded surface. A subsequent coat can be applied after complete cure and a good sanding with a #280/320 grit paper is necessary to obtain a good adhesion. Eliminate all contact with metallic surfaces. Dry film thickness of topcoat must not exceed 3 mils. Total dry film thickness of system should not exceed 5 mils. Danspeed White cannot be used on metal, old oil or cellulose lacquers. Contact with metal surfaces should be avoided once it has been catalyzed. Danspeed White must not be polluted with oil, varnish or the like and must not be sanded with steel wool between coats

To obtain complete cure, the primer must be applied at a temperature above 18ºC and relative humidity below 65%. When drying, this product is not to be exposed to ammonia vapors. Finished surface must not be cleaned with ammonia containing products.

Primers to use with 484-6XXX: 220-005, 220-214, 220-2250, 225-0010, 522-1624, 545-8016 and 546-7257.

THE CUSTOMER IS RESPONSIBLE FOR FOLLOWING THE RECOMMENDED APPLICATION PROCEDURES. FAILURE TO ADHERE TO THE RECOMMENDATIONS GIVEN IN THIS DATA SHEET WILL LIKELY RESULT IN UNSATISFACTORY FILM APPEARANCE OR FILM FAILURE. THE COMPLETE COATING SYSTEM SHOULD BE CHECKED FOR REQUIRED PROPERTIES PRIOR TO THE START-UP OF PRODUCTION.

Drying Times

At 20°C (Minimum Required)

Tack Free Time:	Dry to Sand:	Dry to Stack:
20 - 30 minutes	60 - 90 minutes	12 hours

At 50°C (Minimum Required)

Tack Free Time:	Dry to Sand:	Dry to Stack:
Flash off before entering oven	45 - 60 minutes	2 hours

Note:

N/A

---

Dry times are greatly affected by film build, porosity of substrate, air movement as well as heat and humidity. Temperatures are based on actual board temperature. This may vary depending on length of time for boards to reach these temperatures. Minimum curing temperatures of 64°F/18°C must be maintained throughout the curing cycle to achieve the film integrity as stated in product features.