Product Specifications

Viscosity:	Flash Point:	Density (Kg/L):	Solid (% by weight):	Solid (% by volume):	Shelf Life (months):
Zahn #2 signature cup 28 - 32 sec at 25°C	53.6°F (12°C)	1.05	42% ± 2%	28% ± 1%	6

Product Description

VARISET SELECT White Topcoat is a one-component, pigmented pre-catalyzed Reactive Amino Coating (RAC) with great chemical, household and moisture resistance properties. It has excellent coverage, even on MDF core. VARISET SELECT White Topcoat high solids formulation is user friendly, and has excellent feel, appearance and is formulated to provide
maximum color stability. The coating has light stable properties due to the type of resin used.
Special Recognition: Meets Kitchen Cabinet Manufacturer Association (KCMA) Standards.
Recommended: Architectural Woodwork Institute (AWI). System 2.performance standard for chemical and moisture resistance.

Uses

VARISET SELECT White Topcoat is recommended for kitchen cabinets, office and household furniture, as well as other interior wood applications.

Environmental Data (as supplied)

VOC less exempt lb/gal:	VOC lb/gal:	VOC less exempt g/l:	VOC g/l:	VOC lb/lb Solid:	VHAPs lb/lb Solid:
<5.15	<5.15	<590	<590	<1.42	<0.20

Note:

N/A

Application Data

Suggested Uses:	Mixing Ratio:	Pot Life:	Application Viscosity:	Reducer:	Retarder:	Clean-up Solvent:	Recommended Wet Film:	Coverage:
Wood Finish	N/A	N/A	Zahn #2 signature cup 28 - 32 seconds	121-803 or 121-8020	800-5328 EEP	Lacquer Thinner	3 - 5 mils	10 m2/l (394 sq. ft/gal) at 1 mil dry and at 100% transfer efficiency. Coverage will vary depending on method of application or coating thickness.

Note:

N/A

Surface Preparation

Wood substrate must be sanded using 120, 150 or 180 grit stearated paper prior to coating. An appropriate primer is VARISET SELECT Primer or self-seal. When recoating, the previous coat of VARISET SELECT White Topcoat or VARISET SELECT Primer must be sanded and the next coat applied within eight hours. VARISET SELECT White Topcoat cannot be used on metal, old oil or cellulose lacquers.

General Information

Agitate material before use. Always mix VARISET SELECT White Topcoat while adding reducers in the recommended mixing ratios. VARISET SELECT White Topcoat must be agitated thoroughly at all times to ensure product consistency and consistent gloss.
Apply at 3 - 5 mils wet on sanded or primed substrate. Further coats may be applied after complete drying followed by sanding with 280/320 grit stearated paper. Maximum film build of VARISET SELECT White Topcoat should not exceed 4 mils dry.
Maximum film build of total coatings system must not exceed 4 mils dry. The second and subsequent coats must be applied the same as the previous coat is sanded.
Contact with metal surfaces should be avoided.
VARISET SELECT White Topcoat must not be polluted with oil, varnish or the like and must not be sanded with steel wool
between coats. VARISET SELECT White Topcoat must not be used and dried at temperatures below 18°C or relative humidity above 65%. During hardening, the enamel must not be exposed to ammonia vapors. Ammonia cleaners should not be used for cleaning the finished surface. This may accelerate discoloration.

THE CUSTOMER IS RESPONSIBLE FOR FOLLOWING THE RECOMMENDED APPLICATION PROCEDURES. FAILURE TO ADHERE TO THE RECOMMENDATIONS GIVEN IN THIS DATA SHEET WILL LIKELY RESULT IN UNSATISFACTORY FILM APPEARANCE OR FILM FAILURE. THE COMPLETE COATING SYSTEM SHOULD BE CHECKED FOR REQUIRED PROPERTIES PRIOR TO THE START-UP OF PRODUCTION.

Drying Times

At 20°C (Minimum Required)

Tack Free Time:	Dry to Sand:	Dry to Stack:
10 – 20 minutes	2 hours	3 hours

At 50°C (Minimum Required)

Tack Free Time:	Dry to Sand:	Dry to Stack:
Flash off before entering oven	30 - 45 minutes	60 – 90 minutes

Note:

N/A

---

Dry times are greatly affected by film build, porosity of substrate, air movement as well as heat and humidity. Temperatures are based on actual board temperature. This may vary depending on length of time for boards to reach these temperatures. Minimum curing temperatures of 64°F/18°C must be maintained throughout the curing cycle to achieve the film integrity as stated in product features.