Product Specifications

Viscosity:	Flash Point:	Density (lb/gal):	Solid (% by weight):	Solid (% by volume):	Shelf Life (months):
Zahn #2 signature cup 20-22 sec at 77°F	-4° F (-20°C)	7.8	24%	18%	6

Product Description

Airguard is a one-component pre-catalyzed lacquer. Airguard demonstrates very good moisture, household wear, household chemical, solvent and mar resistance.  Airguard is supplied at a ready to spray viscosity.  Airguard does provide a very unique soft feel. 

Special Recognition:  Meets Kitchen Cabinet Manufacturer Association (KCMA) Standards.

Recommended:  Architectural Woodwork Institute (AWI). T.R.2.        

Uses

Airguard is recommended for office and household furniture, kitchen cabinets, as well as many other interior wood applications. 

Environmental Data (as supplied)

VOC less exempt lb/gal:	VOC lb/gal:	VOC less exempt g/l:	VOC g/l:	VOC lb/lb Solid:	VHAPs lb/lb Solid:
<5.64	<5.20	<675	<625	<2.73	<0.02

Note:

N/A

Application Data

Suggested Uses:	Mixing Ratio:	Pot Life:	Application Viscosity:	Reducer:	Retarder:	Clean-up Solvent:	Recommended Wet Film:	Coverage:
Wood Finish	No extra catalyst required	Not applicable	Zahn #2 signature cup 20 – 22 seconds	803-1325 (Maximum 5%)	N/A	Acetone	3 – 5 mils	289 sq ft/gal at 1 mil dry and at 100% transfer efficiency. Coverage will vary depending on method of application or coating thickness.

Note:

N/A

Surface Preparation

Substrate must be sanded using 120, 150 or 180 grit stearated paper prior to staining or coating. Sealers, if used, should be sanded with 280/320 grit stearated paper prior to being coated. The seal coat should be topcoated within (8) hours of being sanded. Airguard must be used as a self-seal. When recoating, the previous coat of Airguard must be sanded, and the next coat applied within (8) hours. Airguard cannot be used on metal, old oil or cellulose lacquers. Stain systems used under Airguard systems should be acid stable. AkzoNobel recommends using 825-90XX, 825-91XX Promatch® C-Mix Stains or 824-50XX Promatch Aqua Stains.

General Information

Agitate material before use. Keep Airguard agitated thoroughly at all times to ensure product consistency and consistent gloss.

Apply at 3 – 5 mill wet on sanded substrate. Further coats may be applied after complete drying followed by sanding with 280/320 grit stearated paper. The second and subsequent coats must be applied the same day as the previous coat is sanded. The maximum film build of Airguard should not exceed 4 mils dry.

This product is intended as a self-seal product. Maximum film build of total coating system must not exceed 4 mils dry. Contact with metal surfaces should be avoided.

Airguard must not be polluted with oil, varnish or the like and must not be sanded with steel wool between coats. Airguard must not be used and dried at temperatures below 64°F or relative humidity above 65%. During hardening the enamel must not be exposed to ammonia vapors. Ammonia cleaners should not be used for cleaning the finished surface. This may accelerate discoloration. 

THE CUSTOMER IS RESPONSIBLE FOR FOLLOWING THE RECOMMENDED APPLICATION PROCEDURES. FAILURE TO ADHERE TO THE RECOMMENDATIONS GIVEN IN THIS DATA SHEET WILL LIKELY RESULT IN UNSATISFACTORY FILM APPEARANCE OR FILM FAILURE. THE COMPLETE COATING SYSTEM SHOULD BE CHECKED FOR REQUIRED PROPERTIES PRIOR TO THE START-UP OF PRODUCTION.

Drying Times

Room Temperature (68°F)

Tack Free Time:	Dry to Sand:	Dry to Stack:
15 – 20 minutes	1 hour	2 hours

Forced Drying Schedule (122°F)

Tack Free Time:	Dry to Sand:	Dry to Stack:
Flash off before entering oven	30 - 45 minutes	60 – 90 minutes

Note:

N/A

---

Dry times are greatly affected by film build, porosity of substrate, air movement as well as heat and humidity. Temperatures are based on actual board temperature. This may vary depending on length of time for boards to reach these temperatures. Minimum curing temperatures of 64°F/18°C must be maintained throughout the curing cycle to achieve the film integrity as stated in product features.