Product Specifications

Viscosity:	Flash Point:	Density (Kg/L):	Solid (% by weight):	Solid (% by volume):	Shelf Life (months):
Zahn #3 signature cup 30-35 sec at 25° F	27° C	1.32	69.7	55.9	24

Product Description

Lucido White High Gloss is a high performance, high sheen, two-component polyurethane coating. Lucido gives excellent depth of image, hardness and chemical resistance. Extremely durable with a great finish feel.

Uses

Great choice for surfaces that require extra chemical resistance. Uses include interior marine and aircraft, cabinetry, store fixtures, and musical instruments.

Environmental Data (as supplied)

VOC less exempt lb/gal:	VOC lb/gal:	VOC less exempt g/l:	VOC g/l:	VOC lb/lb Solid:	VHAPs lb/lb Solid:
<3.44	<3.44	412	412	<0.44	<0.10

Note:

N/A

Application Data

Suggested Uses:	Mixing Ratio:	Pot Life:	Application Viscosity:	Reducer:	Retarder:	Clean-up Solvent:	Recommended Wet Film:	Coverage:
Wood Finishes	1:1 with 876-9701	3-4 hours depending on temperature and humidity	Zahn #2 signature cup 20-25 seconds	803-2000	800-2001 3-5% by volume	800-5500 Acetone	4-6 wet mils	N/A

Note:

MAXIMUM DRY FILM THICKNESS OF THE SYSTEM MUST NOT EXCEED 8 DRY MILS

Surface Preparation

Wood substrate should be sanded with 120 and 150 grit prior to application to ensure good adhesion. Sealers and primers should be well sanded using 240, 280 and 320 grit stearated paper. Suitable primers are polyurethane (536-1700, 536-1701 or 536-1702) or polyester (458-XXXX). For optimal performance primers should be coated within 8 hours of sanding. Care should be taken during sanding to avoid sanding through the primer.

General Information

Mix the desired amount of material and apply 3-5 mils wet. The coating when cured is very suitable to be buffed and polished where dust free conditions are not available. Allow product to cure (>24 hours) prior to buffing to reduce shrink-back. The relative humidity in the application and drying rooms should never exceed 75%. Viscosity on the mixed material should be monitored regularly to maintain a consistent appearance. 

The mixed product contains 876-9701, an isocyanate based co-reactant. Please follow all precautions associated with handling and use of these materials.

THE CUSTOMER IS RESPONSIBLE FOR FOLLOWING THE RECOMMENDED APPLICATION PROCEDURES. FAILURE TO ADHERE TO THE RECOMMENDATIONS GIVEN IN THIS DATA SHEET WILL LIKELY RESULT IN UNSATISFACTORY FILM APPEARANCE OR FILM FAILURE. THE COMPLETE COATING SYSTEM SHOULD BE CHECKED FOR REQUIRED PROPERTIES PRIOR TO THE START-UP OF PRODUCTION.

Drying Times

At 20°C (Minimum Required)

Tack Free Time:	Dry to Sand:	Dry to Stack:
30-45 minutes	8-12 hours	3 hours

At 50°C (Minimum Required)

Tack Free Time:	Dry to Sand:	Dry to Stack:
20-30 minutes	4-6 hours	2 hours

Note:

N/A

---

Dry times are greatly affected by film build, porosity of substrate, air movement as well as heat and humidity. Temperatures are based on actual board temperature. This may vary depending on length of time for boards to reach these temperatures. Minimum curing temperatures of 64°F/18°C must be maintained throughout the curing cycle to achieve the film integrity as stated in product features.