Product Specifications

Viscosity:	Flash Point:	Density (Kg/L):	Solid (% by weight):	Solid (% by volume):	Shelf Life (months):
Zahn #4 signature cup 38 sec at 25°C	4°C	1.33 ± 2% at 25°C	70-71%	53-54%	12

Product Description

High solids post-catalyzed white primer. This product offers excellent filling properties for very high quality finish. Recommended for high gloss finish.

Uses

Used as a protective coatings for wood.
For interior usage only.

Environmental Data (as supplied)

VOC less exempt lb/gal:	VOC lb/gal:	VOC less exempt g/l:	VOC g/l:	VOC lb/lb Solid:	VHAPs lb/lb Solid:
3.27	3.27	393	393	0.42	0.24

Note:

See individual compliance sheets for specific data

Application Data

Suggested Uses:	Mixing Ratio:	Pot Life:	Application Viscosity:	Reducer:	Retarder:	Clean-up Solvent:	Recommended Wet Film:	Coverage:
Spray	10% 999-017 or 873-2400	4 hours, if reduced 10 to 20% with 121-8020	22-30 sec Zahn #2 at 25°C	Lacquer Thiner 121-001/803-1339 or 121-8020 (for recommended viscosity, add 10 to 20% by volume)	800-5328 EEP if needed	Lacquer Thinner	3 - 5 mils wet	20 m2/l (220 pi2/l) at 1 mil dry and at 100% efficiency. Coverage will vary depending on method of application or coating thickness.

Note:

N/A

Surface Preparation

Substrate must be sanded with 120, 150 grit paper, free of dust and other contaminants. Before the application of the topcoat, the Plastiprimer must be sanded with a 280/320 grit paper. The primer must be recovered within 8 hours after sanding. This primer must not be applied over metal, old finish or nitrocellulose lacquer.

General Information

Mix well before and during the addition of catalyst and diluents. To assure consistency, always keep the product under agitation. The Plastiprimer can be applied in one or two layers. A good sanding between coats with paper 240/320 is needed to get a good adhesion. The Plastiprimer must be covered within 8 hours after the sanding. When sanding, it is important not to wear through the surface and to pay particular attention to sharp edges of the profile. This can create a non-uniform thickness of the application. Once catalyzed, avoid all contact with metallic surface. The dry film thickness of the Plastiprimer must not exceed 3 mils. The total dry film thickness of the system should not exceed 5 mils.

To obtain a complete cure, the system should be applied at an ambient temperature above 18°C and a relative humidity below 65%. During curing, this product should not be exposed to ammonia vapors. The finished surface cannot be cleaned with an ammonia-based product. Always use containers and equipment in plastic or stainless steel to eliminate any source of discoloration due to oxidation.

Topcoats to use over 220-005: 117-30XX, 117-32XX, 440-0XX and 484-6XXX.

THE CUSTOMER IS RESPONSIBLE FOR FOLLOWING THE RECOMMENDED APPLICATION PROCEDURES. FAILURE TO ADHERE TO THE RECOMMENDATIONS GIVEN IN THIS DATA SHEET WILL LIKELY RESULT IN UNSATISFACTORY FILM APPEARANCE OR FILM FAILURE. THE COMPLETE COATING SYSTEM SHOULD BE CHECKED FOR REQUIRED PROPERTIES PRIOR TO THE START-UP OF PRODUCTION.

Drying Times

At 20°C (Minimum Required)

Tack Free Time:	Dry to Sand:	Dry to Stack:
20-30 minutes	90-120 minutes	4 - 6 hours

At 50°C (Minimum Required)

Tack Free Time:	Dry to Sand:	Dry to Stack:
Flash off before entering oven	45-60 minutes	2 - 3 hours

Note:

N/A

---

Dry times are greatly affected by film build, porosity of substrate, air movement as well as heat and humidity. Temperatures are based on actual board temperature. This may vary depending on length of time for boards to reach these temperatures. Minimum curing temperatures of 64°F/18°C must be maintained throughout the curing cycle to achieve the film integrity as stated in product features.