Product Specifications

Viscosity:	Flash Point:	Density (Kg/L):	Solid (% by weight):	Solid (% by volume):	Shelf Life (months):
Zahn #2 signature cup 40-44 sec at 25°C	50°F (10°C)	1.17	54.46%	36.30%	12

Product Description

CHEMLIFE 24 PLUS White Primer is a fast drying, acid curing primer for interior use that gives a smooth, dense finish suitable for topcoating to produce very high quality pieces. CHEMLIFE 24 PLUS White Primer provides an excellent base and is extremely easy to sand. Due to its 24 hour pot-life, CHEMLIFE 24 PLUS White Primer provides the customer with minimum waste resulting in lower production costs.

Uses

CHEMLIFE 24 PLUS White Primer is designed for hardwoods and MDF. This product offers excellent filling properties as well as excellent vertical hang.

Environmental Data (as supplied)

VOC less exempt lb/gal:	VOC lb/gal:	VOC less exempt g/l:	VOC g/l:	VOC lb/lb Solid:	VHAPs lb/lb Solid:
<4.45	<4.45	<534	<534	<0.83	<0.16

Note:

See individual compliance sheets for specific data

Application Data

Suggested Uses:	Mixing Ratio:	Pot Life:	Application Viscosity:	Reducer:	Retarder:	Clean-up Solvent:	Recommended Wet Film:	Coverage:
Wood Primer	100 parts 522-2500 to 10 part 873-1251	24 hours	Zahn #2 signature cup 40-44 sec at 25°C	121-803 or 121-8020	800-5328 EEP	Lacquer thinner	5 mils	582 sq. ft/gal (14 m2/l) at 1 mil dry and at 100% transfer efficiency. Coverage will vary depending on method of application or coating thickness.

Note:

N/A

Surface Preparation

Substrate should be sanded using 120, 150 or 180 grit stearated paper. CHEMLIFE 24 PLUS White Primer cannot be used on metal, old oil or cellulose lacquers. A suitable topcoat is CHEMLIFE 24 PLUS White 117-25XX.

General Information

Mix CHEMLIFE 24 PLUS White Primer thoroughly, then catalyze and reduce material as recommended. CHEMLIFE 24 PLUS White Primer must be well mixed while adding catalyst and reducers and must be agitated at all times to ensure product consistency.

CHEMLIFE 24 PLUS White Primer is applied in one or two coats and can be used as a primer for most wood and wood products meant for indoor use. A thorough sanding using 240/320 grit stearated paper between coats is essential for adhesion. The second and subsequent coats must be applied the same day as the previous coat is sanded. Care should be taken to avoid sanding through the primer coat. With profiled edges, care must be taken with sanding of primer to avoid sanding through sharp edges. Complex profiles or profiles with sharp corners may cause difficulties in obtaining an effective primer coat of even thickness. In these cases, profile design must be discussed with your technical representative. Contact with metal surfaces should be avoided once the CHEMLIFE 24 PLUS White Primer has been catalyzed. To ensure proper uniformity, the material should be agitated at all times. Recommended film build of CHEMLIFE 24 PLUS White Primer is not to exceed 4 mils dry. Total recommended film build of CHEMLIFE 24 PLUS White Primer and CHEMLIFE 24 PLUS White is not to exceed 6 mils dry.

CHEMLIFE 24 PLUS White Primer must not be polluted with oil, varnish or the like and must not be sanded with steel wool between the coats. CHEMLIFE 24 PLUS White Primer must not be used and dried at temperatures below 18°C or relative humidity above 65%. During the curing process, the coating must not be exposed to ammonia vapors. Ammonia cleaners should not be used for cleaning the finish surfaces. This may accelerate discoloration.

THE CUSTOMER IS RESPONSIBLE FOR FOLLOWING THE RECOMMENDED APPLICATION PROCEDURES. FAILURE TO ADHERE TO THE RECOMMENDATIONS GIVEN IN THIS DATA SHEET WILL LIKELY RESULT IN UNSATISFACTORY FILM APPEARANCE OR FILM FAILURE. THE COMPLETE COATING SYSTEM SHOULD BE CHECKED FOR REQUIRED PROPERTIES PRIOR TO THE START-UP OF PRODUCTION.

Drying Times

At 20°C (Minimum Required)

Tack Free Time:	Dry to Sand:	Dry to Stack:
10 – 15 minutes	1 hour	4 hours

At 50°C (Minimum Required)

Tack Free Time:	Dry to Sand:	Dry to Stack:
Flash off before entering oven	30 minutes	60 minutes

Note:

N/A

---

Dry times are greatly affected by film build, porosity of substrate, air movement as well as heat and humidity. Temperatures are based on actual board temperature. This may vary depending on length of time for boards to reach these temperatures. Minimum curing temperatures of 64°F/18°C must be maintained throughout the curing cycle to achieve the film integrity as stated in product features.