Product Specifications

Viscosity:	Flash Point:	Density (Kg/L):	Solid (% by weight):	Solid (% by volume):	Shelf Life (months):
Zahn #2 signature cup 22 sec at 25°C	-20°C (-4°F)	0.94	30%	23%	12

Product Description

Varicure is a one-component high solids Pre-Catalyzed Reactive Amino Coating (RAC). This is a fast building Pre-Catalyzed RAC due to its high volume solids (23%). Varicure demonstrates very good moisture, household wear, household chemical, solvent and mar resistance. Varicure has very fast hardness development resulting in early print resistance and packaging. Varicure is supplied at a ready to spray viscosity. This coating will dry quickly and sand easily.

Special Recognition: Meets Kitchen Cabinet Manufacturer Association (KCMA) Standards.Recommended:  Architectural Woodwork Institute (AWI). T.R.2.

Uses

Varicure is recommended for office and household furniture, kitchen cabinets, as well as many other interior wood applications.

Environmental Data (as supplied)

VOC less exempt lb/gal:	VOC lb/gal:	VOC less exempt g/l:	VOC g/l:	VOC lb/lb Solid:	VHAPs lb/lb Solid:
<5.36	<4.93	<643	<591	<2.09	<0.24

Note:

See individual compliance sheets for specific data

Application Data

Suggested Uses:	Mixing Ratio:	Pot Life:	Application Viscosity:	Reducer:	Retarder:	Clean-up Solvent:	Recommended Wet Film:	Coverage:
Spray	3% 999-017 if desired	8 hours if catalyzed	Zahn #2 signature cup 20 - 25 seconds	121-803 or 121-8020	800-5328 EEP	Lacquer Thinner	3-5 wet mils	9 m2/l (100 pi2/l at 1 mil dry and at 100% transfer efficiency. Coverage will vary depending on method of application or coating thickness.

Note:

N/A

Surface Preparation

Substrate must be sanded using 120, 150 or 180 grit stearated paper prior to staining or coating. Sealers, if used, should be sanded with 280/320 grit stearated paper prior to being coated. The sealer should be topcoated within eight hours of being sanded. When recoating, the previous coat of Varicure must be sanded and the next coat applied within eight hours. Varicure cannot be used on metal, old oil or cellulose lacquers. Stain systems used under acid catalyzed systems should be acid stable.

General Information

Agitate material before use.  Always mix Varicure while adding hardener and reducers in the recommended mixing ratios. Varicure must be agitated thoroughly at all times to ensure product consistency and consistent gloss.

Apply at 3 – 5 mill wet on sanded substrate.  Further coats may be applied after complete drying followed by sanding with 280/320 grit stearated paper. The second and subsequent coats must be applied the same day as the previous coat is sanded. The maximum film build of Varicure should not exceed 4 mils dry.

Varicure may be catalyzed to further enhance its durability. Contact your coating supplier for a recommendation.

This product is intended as a self-seal product.

Maximum film build of total coating system must not exceed 4 mils dry. Contact with metal surfaces should be avoided.

Varicure must not be polluted with oil, varnish or the like and must not be sanded with steel wool between coats. Varicure must not be used and dried at temperatures below 18°C or relative humidity above 65%. During hardening the enamel must not be exposed to ammonia vapors. Ammonia cleaners should not be used for cleaning the finished surface. This may accelerate discoloration.

Natural ambering or discoloring in the can may occur over time. Although there may be changes of color in the can as the product ages, this will have little to no effect on the product during application. Storing in locations above recommended room temperatures could accelerate ambering.

This product does contain formaldehyde, but the quantity is below the reportable amount according to OSHA regulation 1910.1048.

THE CUSTOMER IS RESPONSIBLE FOR FOLLOWING THE RECOMMENDED APPLICATION PROCEDURES. FAILURE TO ADHERE TO THE RECOMMENDATIONS GIVEN IN THIS DATA SHEET WILL LIKELY RESULT IN UNSATISFACTORY FILM APPEARANCE OR FILM FAILURE. THE COMPLETE COATING SYSTEM SHOULD BE CHECKED FOR REQUIRED PROPERTIES PRIOR TO THE START-UP OF PRODUCTION.

Drying Times

At 20°C (Minimum Required)

Tack Free Time:	Dry to Sand:	Dry to Stack:
10 - 15 minutes	20 - 30 minutes	2 Hours

At 50°C (Minimum Required)

Tack Free Time:	Dry to Sand:	Dry to Stack:
Flash off before entering oven	15 - 20 minutes	60 - 90 minutes

Note:

N/A

---

Dry times are greatly affected by film build, porosity of substrate, air movement as well as heat and humidity. Temperatures are based on actual board temperature. This may vary depending on length of time for boards to reach these temperatures. Minimum curing temperatures of 64°F/18°C must be maintained throughout the curing cycle to achieve the film integrity as stated in product features.