Product Specifications

Viscosity:	Flash Point:	Density (Kg/L):	Solid (% by weight):	Solid (% by volume):	Shelf Life (months):
90 ± 2 KU at 25°C	-20°C	1.14 ± 2% at 25°C	45%	25%	12

Product Description

This product is a one-component quick drying Pre-Catalyzed Reactive Amino Coating (RAC) basecoat with excellent sanding properties.

Uses

Basecoat blanc is intended for use on interior wood applications.

Environmental Data (as supplied)

VOC less exempt lb/gal:	VOC lb/gal:	VOC less exempt g/l:	VOC g/l:	VOC lb/lb Solid:	VHAPs lb/lb Solid:
5.13	4.96	616	595	1.15	0.60

Note:

See individual compliance sheets for specific data

Application Data

Suggested Uses:	Mixing Ratio:	Pot Life:	Application Viscosity:	Reducer:	Retarder:	Clean-up Solvent:	Recommended Wet Film:	Coverage:
Spray	N/A	N/A	According to dilution	1 part of Lacquer Thinner 121-001 / 803-1339 for 2 parts of 225-0010	800-5328 EEP	Lacquer Thinner	3 to 5 mils wet	10 m2/l ( 105pi2/l) at 1 mil dry and at 100% efficiency. Coverage will vary depending on method of application or coating thickness.

Note:

N/A

Surface Preparation

Substrate must be sanded with 120, 150 or 180 grit paper, free of dust and other contaminants. Before the application of the topcoat, the Basecoat must be sanded with a 280/320 grit paper. The Basecoat must be recovered within 8 hours following the sanding. This Basecoat must not be applied over metal, old finish or nitrocellulose lacquer.

General Information

Mix thoroughly and dilute as recommended. To assure consistency, this product should be stir continuously. The Basecoat can be applied in one or two layers. A good sanding between coats with paper 240/320 is needed to get a good adhesion. The Basecoat must be recovered within 8 hours after the sanding. When sanding, it is important not to wear through the surface and to pay particular attention to sharp edges of the profile. This can create a non-uniform thickness of the application. Avoid all contact with metallic surface. The dry film thickness of the Basecoat must not exceed 2 mils. The total dry film thickness of the system should not exceed 4 mils.

To obtain a complete cure, the system should be applied at an ambient temperature above 18°C and a relative humidity below 65%. During curing, this product should not be exposed to ammonia vapors. The finished surface cannot be cleaned with an ammonia-based product. Always use containers and equipment in plastic or stainless steel to eliminate any source of discoloration due to oxidation.

Topcoats to use over 225-0010: 131-50XX, 131-51XX, 117-30XX, 117-32XX, 440-XXX and 484-6XX

THE CUSTOMER IS RESPONSIBLE FOR FOLLOWING THE RECOMMENDED APPLICATION PROCEDURES. FAILURE TO ADHERE TO THE RECOMMENDATIONS GIVEN IN THIS DATA SHEET WILL LIKELY RESULT IN UNSATISFACTORY FILM APPEARANCE OR FILM FAILURE. THE COMPLETE COATING SYSTEM SHOULD BE CHECKED FOR REQUIRED PROPERTIES PRIOR TO THE START-UP OF PRODUCTION.

Drying Times

At 20°C (Minimum Required)

Tack Free Time:	Dry to Sand:	Dry to Stack:
10 - 15 minutes	20 - 30 minutes	2 hours

At 50°C (Minimum Required)

Tack Free Time:	Dry to Sand:	Dry to Stack:
Flash off before entering oven	20 – 30 minutes	60 minutes

Note:

N/A

---

Dry times are greatly affected by film build, porosity of substrate, air movement as well as heat and humidity. Temperatures are based on actual board temperature. This may vary depending on length of time for boards to reach these temperatures. Minimum curing temperatures of 64°F/18°C must be maintained throughout the curing cycle to achieve the film integrity as stated in product features.