Product Specifications

Viscosity:	Flash Point:	Density (Kg/L):	Solid (% by weight):	Solid (% by volume):	Shelf Life (months):
Zahn #2 signature cup 58 sec at 25ºC	-3ºC (27ºF)	1.11	50%	34%	12

Product Description

Optiprime is a one-component, high solids, Pre-Catalyzed Reactive Amino Coating (RAC) used as a primer.It has good filling properties and hiding characteristics. This coating may be catalyzed to further enhance its durability. Contact your coating supplier for a recommendation.

Uses

Interior wood applications

Environmental Data (as supplied)

VOC less exempt lb/gal:	VOC lb/gal:	VOC less exempt g/l:	VOC g/l:	VOC lb/lb Solid:	VHAPs lb/lb Solid:
5.26	5.26	631	631	1.42	0.32

Note:

See individual compliance sheets for specific data

Application Data

Suggested Uses:	Mixing Ratio:	Pot Life:	Application Viscosity:	Reducer:	Retarder:	Clean-up Solvent:	Recommended Wet Film:	Coverage:
Spray	100 parts by volume, 3 parts by volume of 999-017 Hardener if catalyzed.	8 hours if catalyzed	Zahn #2 signature cup 2 – 25 seconds	Lacquer thinner 121-001/803-1339 or 121-8020	800-5328 EEP	Lacquer Thinner	3 to 5 mils wet	13 m2/l (144 pi2/l) at 1 mil dry and at 100% transfer efficiency. Coverage will vary depending on method of application or coating thickness.

Note:

N/A

Surface Preparation

Substrate should be sanded using 120, 150 or 180 grit stearated paper prior to coating. Primers, if used, should be sanded prior to being coated with 280/320 grit stearated paper. When recoating, the previous coat of Optiprime must be sanded and the next coat applied within eight hours. Optiprime cannot be used on metal, old oil or cellulose lacquers.

General Information

Agitate material before use. Always mix Optiprime while adding hardener and reducers in the recommended mixing ratios. Optiprime must be agitated thoroughly at all times to ensure product consistency.
Apply at 3-5 mils wet on sanded substrate. Further coats may be applied after complete drying followed by sanding with 280/320 grit stearated paper. The second and subsequent coats must be applied the same day as the previous coat is sanded.
Maximum film build of Optiprime should not exceed 2-3 mils dry. Maximum film build of total coating system must not exceed 4
mils dry. Contact with metal surfaces should be avoided.
Optiprime must not be polluted with oil, varnish or the like and must not be sanded with steel wool between the coats. Optiprime
must not be used and dried at temperatures below 18°C or relative humidity above 65%. During hardening the enamel must not be exposed to ammonia vapors. Ammonia cleaners should not be used for cleaning the finished surface.This may accelerate discoloration.

Topcoats to use over 545-8006: 131-51XX, 131-82XX, 431-90XX, 431-98XX.

THE CUSTOMER IS RESPONSIBLE FOR FOLLOWING THE RECOMMENDED APPLICATION PROCEDURES. FAILURE TO ADHERE TO THE RECOMMENDATIONS GIVEN IN THIS DATA SHEET WILL LIKELY RESULT IN UNSATISFACTORY FILM APPEARANCE OR FILM FAILURE. THE COMPLETE COATING SYSTEM SHOULD BE CHECKED FOR REQUIRED PROPERTIES PRIOR TO THE START-UP OF PRODUCTION.

Drying Times

At 20°C (Minimum Required)

Tack Free Time:	Dry to Sand:	Dry to Stack:
10 - 15 minutes	1 - 2 hours	3 hours

At 50°C (Minimum Required)

Tack Free Time:	Dry to Sand:	Dry to Stack:
Flash off before entering oven	30 minutes	60 - 90 minutes

Note:

N/A

---

Dry times are greatly affected by film build, porosity of substrate, air movement as well as heat and humidity. Temperatures are based on actual board temperature. This may vary depending on length of time for boards to reach these temperatures. Minimum curing temperatures of 64°F/18°C must be maintained throughout the curing cycle to achieve the film integrity as stated in product features.