Product Specifications

Viscosity:	Flash Point:	Density (Kg/L):	Solid (% by weight):	Solid (% by volume):	Shelf Life (months):
Zahn #4 signature cup 53 sec at 25°C	>93°C (200F)	1.18	47 ± 1%	37 ± 1%	12

Product Description

Acryllak White is an acrylic modified polyurethane waterborne solid colour finish. Acryllak is a wear resistant, fast drying and environmentally friendly pigmented lacquer. It is resistant to conventional detergents and household cleaners.

Uses

Acryllak is designed for wooden surfaces in general, and can be used as a topcoat for waterborne primers. It can be used for various surfaces when properly prepared. The inherently high viscosity allows this product to be applied by roller or brush as well.

Environmental Data (as supplied)

VOC less exempt lb/gal:	VOC lb/gal:	VOC less exempt g/l:	VOC g/l:	VOC lb/lb Solid:	VHAPs lb/lb Solid:
11.43	5.17	215	102	0.18	0.09

Note:

See individual compliance sheets for specific data

Application Data

Suggested Uses:	Mixing Ratio:	Pot Life:	Application Viscosity:	Reducer:	Retarder:	Clean-up Solvent:	Recommended Wet Film:	Coverage:
Pigmented Waterborne Topcoat	N/A	N/A	Zahn #4 signature cup 53 seconds	Water, Use less than 5%, viscosity drops quickly	N/A	Use water when wet, 4:1 water:800-5742 if dried	3-5 mils wet	N/A

Note:

N/A

Surface Preparation

Substrate to be coated should be sanded with 150 or 180 grit sandpaper prior to coating. This product should be primed using Aquaprime.

General Information

Add water as required and mix material before use. Apply by spray at wet film builds of 3-5 mils. Application and drying conditions must be at temperatures of 18°C or higher and at a humidity of less than 65%. Increased air flow or drying temperatures, including the use of infrared, will greatly decrease dry times.
Further coats may be applied after complete drying followed by sanding with 280/320 grit sandpaper. Second coat must be applied the same day as the board is sanded.
Product must be agitated thoroughly at all times to ensure product consistency. Contact with metal surfaces should be avoided. Film build should not exceed 2 dry mils per coat.
Total film build must not exceed 5 dry mils.

THE CUSTOMER IS RESPONSIBLE FOR FOLLOWING THE RECOMMENDED APPLICATION PROCEDURES. FAILURE TO ADHERE TO THE RECOMMENDATIONS GIVEN IN THIS DATA SHEET WILL LIKELY RESULT IN UNSATISFACTORY FILM APPEARANCE OR FILM FAILURE. THE COMPLETE COATING SYSTEM SHOULD BE CHECKED FOR REQUIRED PROPERTIES PRIOR TO THE START-UP OF PRODUCTION.

Drying Times

At 20°C (Minimum Required)

Tack Free Time:	Dry to Sand:	Dry to Stack:
20 minutes	2 - 3 hours	24 hours

At 50°C (Minimum Required)

Tack Free Time:	Dry to Sand:	Dry to Stack:
Flash off before entering oven	60 minutes	8 hours

Note:

N/A

---

Dry times are greatly affected by film build, porosity of substrate, air movement as well as heat and humidity. Temperatures are based on actual board temperature. This may vary depending on length of time for boards to reach these temperatures. Minimum curing temperatures of 64°F/18°C must be maintained throughout the curing cycle to achieve the film integrity as stated in product features.