109-4995 Selva™ Pro Lucido Polyurethane High Gloss White Topcoat
Product Codes:

109-4995

Surface Preparation:

Wood substrate should be sanded with 120 and 150 grit prior to application to ensure good adhesion. Sealers and primers should be well sanded using 320 grit stearated paper. Suitable primers are polyurethane (536-1700, 536-1701 or 536-1702) or polyester (458-XXXX). For optimal performance primers should be coated within 8 hours of sanding. Care should be taken during sanding to avoid sanding through the primer.


General Information:

Mix the desired amount of material and apply 3-5 mils wet. The coating when cured is very suitable to be buffed and polished where dust free conditions are not available. Allow product to cure (>24 hours) prior to buffing to reduce shrink-back. The relative humidity in the application and drying rooms should never exceed 75%. Viscosity on the mixed material should be monitored regularly to maintain a consistent appearance.

The mixed product contains 876-9701, an isocyanate based co-reactant. Please follow all precautions associated with handling and use of these materials.


PDF Name: US-PIS_109-4995_Selva_Pro_Lucido_Polyurethane_High_Gloss_White_Topcoat
Tack Free Time: 30-45 minutes
Files: US-PIS_109-4995_Selva_Pro_Lucido_Polyurethane_High_Gloss_White_Topcoat.pdf
Dry to Sand : 3 hours
Dry to Stack: 8 - 12 hours
Tack Free Time: 20-30 minutes
VOC less exempt lb/gal: <3.44
Dry to Sand: 2 hours
VOC lb/gal: <3.44
VOC less exempt g/l: 412
VOC g/l: 412
VOC lb/lb Solid: <0.44
Dry to Stack: 4 - 6 hours
VHAPs lb/lb Solid: <0.10
Note: N/A
Note:

N/A

spec_description:

Selva Pro Lucido White High Gloss is a high-performance, wet-look, two-component polyurethane coating. It can be cut and polished easily making it ideal for high-end woodwork offering high build with high gloss retention and clarity. It can be tinted with 844 tints for a variety of pastel shades. 

spec_uses:

Great choice where a very high gloss finished is required.  Uses include interior cabinetry, interior marine and aircraft cabinetry, store fixtures, and musical instruments.

Suggested Uses: Wood Finishes
Mixing Ratio:

1:1 with 876-9701

Pot Life: 3-4 hours depending on temperature and humidity
Application Viscosity:

Zahn #2 signature cup 20-25 seconds.

Reducer: 803-2000
Retarder: 800-2001 3-5% by volume
Clean-up Solvent: 800-5500 Acetone
Recommended Wet Film: 4-6 wet mils
Coverage:

N/A

Note application:

MAXIMUM DRY FILM THICKNESS OF THE SYSTEM MUST NOT EXCEED 8 DRY MILS


Viscosity:

Zahn #3 signature cup 30-35 sec at 77° F

Flash Point: 80.6° F
Density (lb/gal): 11.33
Solid (% by weight): 69.7
Solid (% by volume): 55.9
Shelf Life (months): 24

Selva Pro

109-4995 Selva™ Pro Lucido Polyurethane High Gloss White Topcoat

Find distributor Trouver un distributeur

spec_description:

Selva Pro Lucido White High Gloss is a high-performance, wet-look, two-component polyurethane coating. It can be cut and polished easily making it ideal for high-end woodwork offering high build with high gloss retention and clarity. It can be tinted with 844 tints for a variety of pastel shades. 

Read more

Selva Pro

109-4995 Selva™ Pro Lucido Polyurethane High Gloss White Topcoat

spec_description:

Selva Pro Lucido White High Gloss is a high-performance, wet-look, two-component polyurethane coating. It can be cut and polished easily making it ideal for high-end woodwork offering high build with high gloss retention and clarity. It can be tinted with 844 tints for a variety of pastel shades. 

Read more
Product codeCodes de produit
Product Codes:

109-4995


Product information

Product specificationsSpécifications du produit

Viscosity:

Zahn #3 signature cup 30-35 sec at 77° F

Flash Point: 80.6° F
Density (lb/gal): 11.33
Solid (% by weight): 69.7
Solid (% by volume): 55.9
Shelf Life (months): 24

Download product information sheets

These products are designed for industrial use only. AkzoNobel views safety as a top priority. Please refer to Material Safety Data Sheet for information on the safe use of this product.

Dry times are greatly affected by film build, porosity of substrate, air movement as well as heat and humidity. Temperatures are based on actual board temperature. This may vary depending on length of time for boards to reach these temperatures. Minimum curing temperatures of 64°F/18°C must be maintained throughout the curing cycle to achieve the film integrity as stated in product features.

Image

Recommended for interior woodwork

OmniBuild Pro Conversion Varnish Primer Surfacer is recommended for interior woodwork on solid wood and MDF.

Recommandé pour les boiseries intérieures

OmniBuild Pro Conversion Varnish Primer Surfacer est recommandé pour les travaux de menuiserie intérieure sur bois massif et MDF.

View our ranges

Our extensive wood coatings expertise covers all technologies. From pre-catalyzed to waterborne, nitrocellulose to polyurethane, we deliver a wide range of top-performing products for your business.

View our ranges

Our extensive wood coatings expertise covers all technologies. From pre-catalyzed to waterborne, nitrocellulose to polyurethane, we deliver a wide range of top-performing products for your business.

Need help? Contact our team of wood coating experts.

Contact us