GLAZE

825-4010 Promatch® Chemglaze 275 SB Stain

Product Codes:

825-4010

Surface Preparation:

Substrate must be sanded using 120, 150 or 180 grit stearated paper prior to glazing. Sealers should be sanded immediately prior to being coated with 280/320 grit stearated paper. Appropriate sealers are Chemcraft 275 sealers.

General Information:

Agitate material before use. Chemglaze 275 must be agitated thoroughly at all times to ensure product consistency and consistent gloss. After application and wiping, brush blending, highlighting and drying, Chemglaze can topcoated by system-suitable Chemcraft 275 topcoats. Application by spray. After application, allow one or two minutes and then the product can be wiped, brushed and highlighted. Wipe clean and remove any excess glaze to ensure optimum adhesion by subsequent clear coats. Adhesion of the system must be thoroughly checked as the type of coatings used, the amount of glaze applied and wiped off and the time of dry all affect the overall system adhesion. As a rule vinyl sealers provide improved adhesion characteristics.

Chemglaze 275 SB Stain 825-4010 may be tinted with up to 15% by volume of 824 line G-P-D colorants from. All systems must be checked for suitable adhesion and film properties before use. It may be clear coated with any of the Chemcraft solvent based products Chemlack 275 441-51XX, EVar 275 421-84XX, Varicure® 275 431-17XX and Chemlack Express 275 441-22XX as well as the sealers associated with these systems.
Please note that in systems containing catalyzed or pre-catalyzed coatings, such as Plastofix and Opticlear, the coating under the glaze should be sanded and the topcoat must be applied within eight (8) hours of the first coating being sanded.

PDF Name: US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain, US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain

Tack Free Time: N/A

Files: US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain.pdf

Dry to Sand : N/A

Dry to Stack: N/A

Tack Free Time: N/A

VOC less exempt lb/gal: <2.4

Dry to Sand: N/A

VOC lb/gal: <2.2

VOC less exempt g/l: <290

VOC g/l: <260

VOC lb/lb Solid: <0.40

Dry to Stack: N/A

VHAPs lb/lb Solid: <0.01

Note: N/A

Note:

See individual compliance sheets for specific data

spec_description:

Chemglaze 275 SB Stain 825-4010 is a low VOC glaze that demonstrates good open time to allow for workability on large pieces. When applied correctly, tinted Chemglaze will enhance the natural beauty of the wood.

spec_uses:

Chemglaze 275 SB Stain 825-4010 is an all-purpose neutral glaze for furniture, millwork and cabinets.

Suggested Uses:

Wood Glaze

Mixing Ratio:

N/A

Pot Life:

N/A

Application Viscosity:

Zahn #2 signature cup 20 seconds

Reducer: N/A

Retarder: N/A

Clean-up Solvent: 800-5500

Recommended Wet Film: N/A

Coverage:

Coverage will vary depending on method of application and required color depth.

Note application:

N/A

Viscosity:

Zahn #2 signature cup 20 sec at 77°F

Flash Point: 55°F (13°C)

Density (lb/gal): 8.6

Solid (% by weight): 62%

Solid (% by volume): 60%

Shelf Life (months): 12

GLAZE

825-4010 Promatch® Chemglaze 275 SB Stain

Find distributor Trouver un distributeur

spec_description:

BACK

GLAZE

825-4010 Promatch® Chemglaze 275 SB Stain

spec_description:

Product codeCodes de produit
Product Codes:

825-4010

Product information

Product specificationsSpécifications du produit

Viscosity:

Zahn #2 signature cup 20 sec at 77°F

Flash Point: 55°F (13°C)

Density (lb/gal): 8.6

Solid (% by weight): 62%

Solid (% by volume): 60%

Shelf Life (months): 12

UsesUtilisations

Environmental data (as supplied)Données environmentales (tel que fourni)

Application dataDonnées d'application

Surface PreparationPréparation de la surface

General InformationInformations générales

Drying TimesTemps de séchage

Find distributor Trouver un distributeur

Download product information sheets

Files: US-PIS_825-4010_Promatch_Chemglaze_275_SB_Stain.pdf

These products are designed for industrial use only. AkzoNobel views safety as a top priority. Please refer to Material Safety Data Sheet for information on the safe use of this product.

Dry times are greatly affected by film build, porosity of substrate, air movement as well as heat and humidity. Temperatures are based on actual board temperature. This may vary depending on length of time for boards to reach these temperatures. Minimum curing temperatures of 64°F/18°C must be maintained throughout the curing cycle to achieve the film integrity as stated in product features.

Recommended for interior woodwork

OmniBuild Pro Conversion Varnish Primer Surfacer is recommended for interior woodwork on solid wood and MDF.

Recommandé pour les boiseries intérieures

OmniBuild Pro Conversion Varnish Primer Surfacer est recommandé pour les travaux de menuiserie intérieure sur bois massif et MDF.

View our ranges

Our extensive wood coatings expertise covers all technologies. From pre-catalyzed to waterborne, nitrocellulose to polyurethane, we deliver a wide range of top-performing products for your business.

Learn more

View our ranges

Our extensive wood coatings expertise covers all technologies. From pre-catalyzed to waterborne, nitrocellulose to polyurethane, we deliver a wide range of top-performing products for your business.

Learn more

About our brand	Products	Distributors	Using our products
Contact us	Pre-Catalyzed	Our Distributors	How-to-videos
	Post-Catalyzed	Our Ordering portals	Troubleshooting Guides
	Polyurethane		Glossary of Terms
	Waterborne		Associations
	Color Systems		Mobile Product App
	Vinyl Products
	Nitrocellulose
	Specialty Products

Cookies	Cookie settings	Privacy	Sitemap