117-55XX Plasticolor White RTS Conversion Varnish Pigmented Topcoat
Product Codes:

117-5510 10° Matte
117-5520 20° Low Gloss
117-5535 35° Satin
117-5550 50° Semi-Gloss

Surface Preparation:

Primer should be sanded using #280/320 grit stearated paper before application of the topcoat and must be recovered withing 8 hours after sanding. Care should be taken during sanding to avoid sanding through the primer. Plasticolor White must not be applied over metal, old oil finish or nitrocellulose lacquer. 

General Information:

Plasticolor enamel must be thoroughly stirred, while adding hardener and reducers in the recommended ration.  To ensure proper sheen, the catalyzed material should be agitated at all times. Apply 3 - 5 mils wet on sanded surface. A subsequent coat can be applied after complete cure, and a good sanding with #280/320 grit paper is necessary to obtain a good adhesion.  The subsequent coat must be applied the same day as the previous coat is sanded. Dry film thickness of topcoat must not exceed 3 mils.  Total dry film thickness of system should not exceed 6 mils. Plasticolor must not be polluted with oil, varnish or the like and must not be sanded with steel wool between coats. Contact with metal surfaces should be avoided once the Plasticolor White RTS has been catalyzed. 
To obtain complete cure, the Plasticolor must be applied at a temperature above 18ºC and relative humidity below 65%.  When drying, this product is not to be exposed to ammonia vapors. Finished surface must not be cleaned with ammonia containing products. 

Primers to use with 117-55XX Plasticolor White RTS Conversion Varnish Pigmented Topcoat are:
220-214 Plastiprimer Off White Post-Cat Pigmented Primer
522-1410 Plastiprimer 900 White Post-Cat Pigmented Primer

PDF Name: CA-PIS_117-55XX_Plasticolor_White_RTS_Conversion_Varnish_Pigmented_Topcoat
Tack Free Time: 30 – 45 minutes
Files: CA-PIS_117-55XX_Plasticolor_White_RTS_Conversion_Varnish_Pigmented_Topcoat.pdf
Dry to Sand : 90 - 120 minutes
Dry to Stack: 12 hours
Tack Free Time: Flash off before entering oven
Dry to Sand: 45-60 minutes
VOC less exempt g/l: 520
VOC g/l: 520
Dry to Stack: 2 hours
Note: N/A
Note:

See individual compliance sheet for specific data.

spec_description:

Plasticolor White RTS is a ready to use, acid curing high-solids fast drying Reactive Amino Coating (RAC). This is a fast building product due to its high solid content (38% by volume).  It gives a smooth, knock-proof and hardwearing surface resisting influence from alcohol, water, etc. This pigmented conversion varnish has very good light stability based on the type of resin used. 

spec_uses:

Plasticolor White RTS is used as the final coat over wood, plywood, chipboard, etc. meant for interior use. This product is recommended for kitchen cabinets, high build office or residential furniture as well as many other interior wood applications where high build and durability are required. 

Suggested Uses: Spray
Mixing Ratio:

8% 999-017 or 999-031A

Pot Life: 8 hours
Application Viscosity:

Zahn #2 signature cup, 19-23 sec at 25°C

Reducer: 121-8020 ir 121-803 if necessary
Retarder: 800-5328 EEP (2-3% maximum)
Clean-up Solvent: Lacquer Thinner
Recommended Wet Film: 3 - 5 mils
Coverage:

16 m2/l (172 pi2/l) at 1 mil dry and at 100% efficiency. Coverage will vary depending on method of application or coating thickness.


Note application:

N/A

Viscosity:

Zahn #4 signature cup, 21 sec at 25°C

Flash Point: 4°C
Density (lb/gal): 1.10 ± 2% at 25°C
Solid (% by weight): 53 ± 1%
Solid (% by volume): 38 ± 1%
Shelf Life (months): 12

Plasticolor

117-55XX Plasticolor White RTS Conversion Varnish Pigmented Topcoat

Find distributor Trouver un distributeur

spec_description:

Plasticolor White RTS is a ready to use, acid curing high-solids fast drying Reactive Amino Coating (RAC). This is a fast building product due to its high solid content (38% by volume).  It gives a smooth, knock-proof and hardwearing surface resisting influence from alcohol, water, etc. This pigmented conversion varnish has very good light stability based on the type of resin used. 

Read more

Plasticolor

117-55XX Plasticolor White RTS Conversion Varnish Pigmented Topcoat

spec_description:

Plasticolor White RTS is a ready to use, acid curing high-solids fast drying Reactive Amino Coating (RAC). This is a fast building product due to its high solid content (38% by volume).  It gives a smooth, knock-proof and hardwearing surface resisting influence from alcohol, water, etc. This pigmented conversion varnish has very good light stability based on the type of resin used. 

Read more
Product codeCodes de produit
Product Codes:

117-5510 10° Matte
117-5520 20° Low Gloss
117-5535 35° Satin
117-5550 50° Semi-Gloss


Product information

Product specificationsSpécifications du produit

Viscosity:

Zahn #4 signature cup, 21 sec at 25°C

Flash Point: 4°C
Density (lb/gal): 1.10 ± 2% at 25°C
Solid (% by weight): 53 ± 1%
Solid (% by volume): 38 ± 1%
Shelf Life (months): 12

Download product information sheets

These products are designed for industrial use only. AkzoNobel views safety as a top priority. Please refer to Material Safety Data Sheet for information on the safe use of this product.

Dry times are greatly affected by film build, porosity of substrate, air movement as well as heat and humidity. Temperatures are based on actual board temperature. This may vary depending on length of time for boards to reach these temperatures. Minimum curing temperatures of 64°F/18°C must be maintained throughout the curing cycle to achieve the film integrity as stated in product features.

Image

Recommended for interior woodwork

OmniBuild Pro Conversion Varnish Primer Surfacer is recommended for interior woodwork on solid wood and MDF.

Recommandé pour les boiseries intérieures

OmniBuild Pro Conversion Varnish Primer Surfacer est recommandé pour les travaux de menuiserie intérieure sur bois massif et MDF.

View our ranges

Our extensive wood coatings expertise covers all technologies. From pre-catalyzed to waterborne, nitrocellulose to polyurethane, we deliver a wide range of top-performing products for your business.

View our ranges

Our extensive wood coatings expertise covers all technologies. From pre-catalyzed to waterborne, nitrocellulose to polyurethane, we deliver a wide range of top-performing products for your business.

Need help? Contact our team of wood coating experts.

Contact us