Plasticolor
117-32XX Plasticolor White Conversion Varnish Pigmented Topcoat
Product Codes:
117-3210 10° Matte
117-3220 20° Low Gloss
117-3235 35° Satin
117-3250 50° Semi-Gloss
117-3290 90° High Gloss
Surface Preparation:
Primer should be sanded using #280/320 grit stearated paper before application of the topcoat and must be recovered within 8 hours after sanding. Care should be taken during sanding to avoid sanding through the primer. Plasticolor White must not be applied over metal, old oil finish or nitrocellulose lacquer.
General Information:
Catalyze and reduce material as recommended. Contact with metal surfaces should be avoided once the Plasticolor White has been catalyzed. To ensure proper sheen, the catalyzed material should be agitated at all times. Plasticolor enamel must be thoroughly stirred, while adding hardener and reducers in the recommended ratio. Apply 3-5 mils wet on sanded surface. A subsequent coat can be applied after complete cure and a good sanding with a #280/320 grit paper is necessary to obtain a good adhesion. Dry film thickness of topcoat must not exceed 3 mils. Total dry film thickness of system should not exceed 6 mils.
Gloss Plasticolor may be rubbed and polished to a dirt free high gloss finish. Polishing methods should be discussed with your technical representative.
To obtain complete cure, the primer must be applied at a temperature above 18ºC and relative humidity below 65%. When drying, this product is not to be exposed to ammonia vapors. Finished surface must not be cleaned with ammonia containing products.
Primers to use with 117-32XX: 220-005, 220-214, 220-2250, 225-0010, 522-1410, 522-1624, 545-8016 and 546-7257.
PDF Name: CA-PIS_117-32XX_Plasticolor_White_Conversion_Varnish_Pigmented_Topcoat
Tack Free Time: 30-45 minutes
Files: CA-PIS_117-32XX_Plasticolor_White_Conversion_Varnish_Pigmented_Topcoat.pdf
Dry to Sand : 90-120 minutes
Dry to Stack: 12 hours
Tack Free Time: Flash off before entering oven
Dry to Sand: 45-60 minutes
VOC less exempt g/l: 402
VOC g/l: 402
Dry to Stack: 2 hours
Note: N/A
Note:
See individual compliance sheets for specific data
spec_description:
Plasticolor White is an acid curing high-solids fast drying Reactive Amino Coating (RAC) with good building properties. This is a fast building product due to its high solid content (52% volume). It gives a smooth, knock-proof and hardwearing surface resisting influence from alcohol, water, etc. This pigmented conversion varnish has very good light stability based on the type of resin used.
spec_uses:
Plasticolor White is used as the final coat over wood, plywood, chipboard, etc. meant for interior use. This product is recommended for kitchen cabinets, high build office or residential furniture as well as many other interior wood applications where high build and durability are required.
Suggested Uses:
Spray
Mixing Ratio:
10% 999-017
Pot Life: 8 hours
Application Viscosity:
20-25 sec Zahn #2 at 25°C
Reducer: 121-8020 or 121-803
Retarder: 800-5328 EEP
Clean-up Solvent: Lacquer Thinner
Recommended Wet Film: 3 to 5 mils wet
Coverage:
20 m²/l (220 pi²/l) at 1 mil dry and at 100% efficiency. Coverage will vary depending on method of application or coating thickness.
Note application:
N/A
Viscosity:
Zahn #3 signature cup 24 sec at 25°C
Flash Point: 20°C
Density (lb/gal): 1.21 ± 2% at 25°C
Solid (% by weight): 67 ± 1%
Solid (% by volume): 52 ± 1%
Shelf Life (months): 12

Plasticolor

117-32XX Plasticolor White Conversion Varnish Pigmented Topcoat

Find distributor Trouver un distributeur

spec_description:

Plasticolor White is an acid curing high-solids fast drying Reactive Amino Coating (RAC) with good building properties. This is a fast building product due to its high solid content (52% volume). It gives a smooth, knock-proof and hardwearing surface resisting influence from alcohol, water, etc. This pigmented conversion varnish has very good light stability based on the type of resin used.

BACKRetour

Product codeCodes de produit
Product Codes:

117-3210 10° Matte
117-3220 20° Low Gloss
117-3235 35° Satin
117-3250 50° Semi-Gloss
117-3290 90° High Gloss

Product information

Product specificationsSpécifications du produit

Viscosity:
Zahn #3 signature cup 24 sec at 25°C
Flash Point: 20°C
Density (lb/gal): 1.21 ± 2% at 25°C
Solid (% by weight): 67 ± 1%
Solid (% by volume): 52 ± 1%
Shelf Life (months): 12

UsesUtilisations

Environmental data (as supplied)Données environnementales (tel que fourni)

Application dataDonnées d'application

Surface PreparationPréparation de la surface

General InformationInformations générales

Drying TimesTemps de séchage

Find distributor Trouver un distributeur

Download product information sheets

Files: CA-PIS_117-32XX_Plasticolor_White_Conversion_Varnish_Pigmented_Topcoat.pdf

These products are designed for industrial use only. AkzoNobel views safety as a top priority. Please refer to Material Safety Data Sheet for information on the safe use of this product.

Dry times are greatly affected by film build, porosity of substrate, air movement as well as heat and humidity. Temperatures are based on actual board temperature. This may vary depending on length of time for boards to reach these temperatures. Minimum curing temperatures of 64°F/18°C must be maintained throughout the curing cycle to achieve the film integrity as stated in product features.

Recommanded for interior woodwork

OmniBuild Pro Conversion Varnish Primer Surfacer is recommended for interior woodwork on solid wood and MDF.

Recommandé pour les boiseries intérieures

OmniBuild Pro, apprêt à catalyser est recommandé pour les travaux de menuiserie intérieure sur bois massif et MDF.

View our ranges

Our extensive wood coatings expertise covers all technologies. From pre-catalyzed to waterborne, nitrocellulose to polyurethane, we deliver a wide range of top-performing products for your business.

Learn more