LUCIDO White High Gloss PU Pigmented TC

109-1890 LUCIDO White High Gloss PU Pigmented TC

Product Codes:

109-1890

Surface Preparation:

Substrate must be sanded using 120, 150 or 180 grit paper prior to staining or coating. Sealer/Primer should be sanded with 280/320 grit paper prior to being coated. The primer should be coated within eight hours of being sanded. Appropriate primer is Verde Bianco Primers 536-1253 or 536-1208 . If recoating, the previous coat must be sanded and the next coat applied within eight hours.

General Information:

The mixed product contains 876-9068, an isocyanate based co-reactant. Please follow all precautions associated with handling and use of those materials. Refer to MSDS for detail information.

When coating exotic woods (Teak, Rosewood, etc.) a barrier coat (tie-coat) should be applied before the sealer or base coat. See Product data sheet for 401-033 Isolante.

Product must be thoroughly stirred before adding the hardener in the recommended ratio. The viscosity of the product should be monitored after mixing with the hardener.

The relative humidity in the application and drying room should not exceed 75% for maximum coating performance.

PDF Name: US-PIS_109-1890_LUCIDO_White_High_Gloss_PU_Pigmented_TC

Tack Free Time: 15 minutes

Files: US-PIS_109-1890_LUCIDO_White_High_Gloss_PU_Pigmented_TC.pdf

Dry to Sand : 3 hours

Dry to Stack: 24 hours

Tack Free Time: 15 minutes

VOC less exempt lb/gal: <3.44

Dry to Sand: 30 minutes

VOC lb/gal: <3.44

VOC less exempt g/l: <415

VOC g/l: <415

VOC lb/lb Solid: <0.44

Dry to Stack: 60 minutes

VHAPs lb/lb Solid: <0.10

Note: N/A

Note:

N/A

spec_description:

Lucido White High Gloss is a high performance, high sheen, two-component polyurethane coating. Lucido gives excellent depth of image, hardness and chemical resistance. Extremely durable with a great finish feel.

spec_uses:

Great choice for surfaces that require extra chemical resistance. Uses include interior marine, cabinetry, store fixture, and musical instruments.

Suggested Uses:

Wood Finish

Mixing Ratio:

100 Parts 109-1890 with 100 Parts 876-9068 (by volume)

Pot Life:

3 - 4 Hours depending on temperature and humidity

Application Viscosity:

Zahn #2 signature cup 20 - 25 seconds

Reducer: Fast 803-5301, or slow 803-5531 if needed

Retarder: 800-5328 3 - 5% by volume

Clean-up Solvent: 800-5500 Acetone or Lacquer Thinners (do not mix with product)

Recommended Wet Film: 3 to 5 wet mils

Coverage:

N/A

Note application:

MAXIMUM DRY FILM THICKNESS OF THE SYSTEM MUST NOT EXCEED 6.0 DRY MILS

Viscosity:

Zahn #3 signature cup 30-35 sec at 77°F

Flash Point: 25° F

Density (lb/gal): 11.33

Solid (% by weight): 69.7

Solid (% by volume): 55.9

Shelf Life (months): 12

LUCIDO White High Gloss PU Pigmented TC

109-1890 LUCIDO White High Gloss PU Pigmented TC

Find distributor Trouver un distributeur

spec_description:

BACK

LUCIDO White High Gloss PU Pigmented TC

109-1890 LUCIDO White High Gloss PU Pigmented TC

spec_description:

Product codeCodes de produit
Product Codes:

109-1890

Product information

Product specificationsSpécifications du produit

Viscosity:

Zahn #3 signature cup 30-35 sec at 77°F

Flash Point: 25° F

Density (lb/gal): 11.33

Solid (% by weight): 69.7

Solid (% by volume): 55.9

Shelf Life (months): 12

UsesUtilisations

Environmental data (as supplied)Données environmentales (tel que fourni)

Application dataDonnées d'application

Surface PreparationPréparation de la surface

General InformationInformations générales

Drying TimesTemps de séchage

Find distributor Trouver un distributeur

Download product information sheets

Files: US-PIS_109-1890_LUCIDO_White_High_Gloss_PU_Pigmented_TC.pdf

These products are designed for industrial use only. AkzoNobel views safety as a top priority. Please refer to Material Safety Data Sheet for information on the safe use of this product.

Dry times are greatly affected by film build, porosity of substrate, air movement as well as heat and humidity. Temperatures are based on actual board temperature. This may vary depending on length of time for boards to reach these temperatures. Minimum curing temperatures of 64°F/18°C must be maintained throughout the curing cycle to achieve the film integrity as stated in product features.

Recommended for interior woodwork

OmniBuild Pro Conversion Varnish Primer Surfacer is recommended for interior woodwork on solid wood and MDF.

Recommandé pour les boiseries intérieures

OmniBuild Pro Conversion Varnish Primer Surfacer est recommandé pour les travaux de menuiserie intérieure sur bois massif et MDF.

View our ranges

Our extensive wood coatings expertise covers all technologies. From pre-catalyzed to waterborne, nitrocellulose to polyurethane, we deliver a wide range of top-performing products for your business.

Learn more

View our ranges

Our extensive wood coatings expertise covers all technologies. From pre-catalyzed to waterborne, nitrocellulose to polyurethane, we deliver a wide range of top-performing products for your business.

Learn more

About our brand	Products	Distributors	Using our products
Contact us	Pre-Catalyzed	Our Distributors	How-to-videos
	Post-Catalyzed	Our Ordering portals	Troubleshooting Guides
	Polyurethane		Glossary of Terms
	Waterborne		Associations
	Color Systems		Mobile Product App
	Vinyl Products
	Nitrocellulose
	Specialty Products

Cookies	Cookie settings	Privacy	Sitemap