AQUASILK 400TW 2K WHITE 228-34XX
Product Codes:
228-3405
228-3410
228-3420
228-3435
228-3450
228-3480
Surface Preparation: Substrate must be sanded using 120, 150 or 180 grit paper prior to priming. Primer should be sanded with 280/320 grit paper prior to being coated, The Primer should be coated within eight hours of being sanded. Appropriate primers are the Chemcraft 550-3500, 550-3501, 550-3502, 550-1600, 550-1602, 550-1760, and 550-1761.. When recoating, the previous coat of the AQUASILK 400TW 2K White Polyurethane Waterborne Topcoat must be sanded and the next coat applied within eight hours of being sanded.
General Information:
**After mixing part A and part B to the correct ratio, water can then be added to reduce viscosity prior to application as needed depending on spray equipment. A maximum of 10% water can be added to the fresh (immediately after the part B is fully dispersed into part A) catalyzed material.

Note: Adding extra water during application is not recommended as this will have a direct impact on the pot life. The pot life of the mixture will be reduced significantly and the mixture will gel quickly.

The mixed product contains 876-3400, an isocyanate based co-reactant. Please follow all precautions associated with handling and use of those materials. Refer to MSDS for detailed information. Product must be thoroughly stirred before adding the hardener in the recommended ratio. The viscosity of the product should be monitored after mixing with the hardener. The relative humidity in the application and drying room should not exceed 75% for maximum coating performance.
PDF Name: US-PIS_AQUASILK_400TW_2K_WHITE_228-34XX
Tack Free Time: 20 minutes
Files: US-PIS_AQUASILK_400TW_2K_WHITE_228-34XX.pdf
Dry to Sand : 45 minutes
Dry to Stack: 24 hours
Tack Free Time: 12 minutes
VOC less exempt lb/gal: 0.34
Dry to Sand: 20 minutes
VOC lb/gal: 0.11
VOC less exempt g/l: N/A
VOC g/l: N/A
VOC lb/lb Solid: 0.02
Dry to Stack: 30 minutes
VHAPs lb/lb Solid: 0.00
Note: N/A
Note:
N/A
spec_description:
AQUASILK 400TW 2K White Topcoat is a white 2K polyurethane waterborne topcoat for industrial application. This product provides excellent water and chemical resistance and has high solids with great hide that allows for ease of application. Whether you are at a finishing shop or at a professional on-site job this low VOC and low odor system meets or exceeds industry standards.
spec_uses:
AQUASILK 400TW 2K White Polyurethane Waterborne Topcoat has been designed for the cabinet, architectural millwork, furniture and refinish markets.
Suggested Uses:
For cabinet, architectural millwork, furniture, refinish markets.
Mixing Ratio:
8% by volume of 876-3400 Hardener
**See Application Data Notes for additional mixing information**
Pot Life:
3-4 hours depending on external condition
Application Viscosity:
Zahn #3 Signature cup 30-35 sec at 77°F (25° C)
Reducer: Water up to 10% by volume
Retarder: 803-1462 1 to 3% by volume
Clean-up Solvent: Water
Recommended Wet Film: 4-5 wet mils
Coverage:
556 sqft/gal
Note application:
AQUASILK 400TW 2K White base should be thoroughly mixed first then hardener must be slowly added during agitation, product must be mixed for 1-2 minutes.

Customer must wait 5 minutes for "induction time" before usage. Mix only what you can use for 2-3 hours at a time. If an excessive amount over 5 wet mils is applied, there is a chance that surface imperfection (mud cracking, etc.) may result.
Viscosity:
Zahn #2 Signature cup 40-45 sec at 77°F (25°C)
Zahn #3 Signature cup 18-22 sec at 77°F (25°C)
Flash Point: Over 200°F (93.3°C)
Density (lb/gal): 10.31 lb/gl
Solid (% by weight): 45.5
Solid (% by volume): 32.5
Shelf Life (months): 12

Waterborne 2K

AQUASILK 400TW 2K WHITE 228-34XX

Find distributor Trouver un distributeur

spec_description:

AQUASILK 400TW 2K White Topcoat is a white 2K polyurethane waterborne topcoat for industrial application. This product provides excellent water and chemical resistance and has high solids with great hide that allows for ease of application. Whether you are at a finishing shop or at a professional on-site job this low VOC and low odor system meets or exceeds industry standards.

BACKRetour

Product codeCodes de produit
Product Codes:

228-3405
228-3410
228-3420
228-3435
228-3450
228-3480

Product information

Product specificationsSpécifications du produit

Viscosity:
Zahn #2 Signature cup 40-45 sec at 77°F (25°C)
Zahn #3 Signature cup 18-22 sec at 77°F (25°C)
Flash Point: Over 200°F (93.3°C)
Density (lb/gal): 10.31 lb/gl
Solid (% by weight): 45.5
Solid (% by volume): 32.5
Shelf Life (months): 12

UsesUtilisations

Environmental data (as supplied)Données environnementales (tel que fourni)

Application dataDonnées d'application

Surface PreparationPréparation de la surface

General InformationInformations générales

Drying TimesTemps de séchage

Find distributor Trouver un distributeur

Download product information sheets

Files: US-PIS_AQUASILK_400TW_2K_WHITE_228-34XX.pdf

These products are designed for industrial use only. AkzoNobel views safety as a top priority. Please refer to Material Safety Data Sheet for information on the safe use of this product.

Dry times are greatly affected by film build, porosity of substrate, air movement as well as heat and humidity. Temperatures are based on actual board temperature. This may vary depending on length of time for boards to reach these temperatures. Minimum curing temperatures of 64°F/18°C must be maintained throughout the curing cycle to achieve the film integrity as stated in product features.

Recommanded for interior woodwork

OmniBuild Pro Conversion Varnish Primer Surfacer is recommended for interior woodwork on solid wood and MDF.

Recommandé pour les boiseries intérieures

OmniBuild Pro, apprêt à catalyser est recommandé pour les travaux de menuiserie intérieure sur bois massif et MDF.

View our ranges

Our extensive wood coatings expertise covers all technologies. From pre-catalyzed to waterborne, nitrocellulose to polyurethane, we deliver a wide range of top-performing products for your business.

Learn more